标题: 紧急求助：MOLDFLOW中结果超过材料的许用剪切率问题 [打印本页]
作者: luminghua88    时间: 2006-10-11 15:51
标题: 紧急求助：MOLDFLOW中结果超过材料的许用剪切率问题
最近我分析了一个汽车上的副仪表板的产品，用的是PP＋20％的碳酸钙，发现在屏幕信息中FILL中显示的摘要中发现最大剪切率超过了材料的最大许用剪切率，这个情况的话，在实际中肯定是不行的，因为材料发生降解了！我想问一下！在MOLDFLOW中除了上述信息中给出提示外，其它地方还会有什么提示，或是显示其危害？我把信息摘录了下 了：

材料数据报告:

制造商                    Ferro
材料编号                      GPP20CS39GY
材料种类                PP
纤维 / 充填物                20% Calcium Carbonate 填充物
Moldflow 材料编号        1052
Moldflow 等级编号         CM1052

Filling phase results summary :

   Maximum injection pressure          (at   2.495 s) =     58.7216 MPa

End of filling phase results summary :

   Time at the end of filling                         =      2.6503 s
   Total weight (part + runners)                      =   1085.4900 g
   Maximum Clamp force - during filling               =    303.8923 tonne
   Recommended ram speed profile (rel):
          % stroke             % speed
     ---------------------------------
            0.0000            16.7004
           10.0000            38.5031
           20.0000            56.9507
           30.0000            80.6993
           40.0000            93.6967
           50.0000           100.0000
           60.0000            95.6350
           70.0000            80.8437
           80.0000            54.4960
           90.0000            37.1491
          100.0000            16.4176
   Melt front is entirely in the cavity at % fill     =      0.0000 %

Filling phase results summary for the part :

   Bulk temperature - maximum          (at   2.506 s) =    239.1300 C
   Bulk temperature - 95th percentile  (at   2.495 s) =    234.4640 C
   Bulk temperature - 5th percentile   (at   2.650 s) =    213.9580 C
   Bulk temperature - minimum          (at   2.650 s) =     73.5270 C

   Wall shear stress - maximum         (at   2.185 s) =      0.3838 MPa
   Wall shear stress - 95th percentile (at   0.116 s) =      0.1708 MPa

   Shear rate - maximum                (at   1.844 s) =  3.4725E+04 1/s
  Shear rate - 95th percentile        (at   0.116 s) =   6074.2798 1/s
End of filling phase results summary for the part :

   Total part weight (excluding runners)              =   1085.4900 g

   Bulk temperature - maximum                         =    237.8060 C
   Bulk temperature - 95th percentile                 =    233.5700 C
   Bulk temperature - 5th percentile                  =    213.9610 C
   Bulk temperature - minimum                         =     73.5270 C
   Bulk temperature - average                         =    222.6170 C
   Bulk temperature - root-mean-square deviation      =     10.9694 C

   Wall shear stress - maximum                        =      0.1983 MPa
   Wall shear stress - 95th percentile                =      0.0894 MPa
   Wall shear stress - average                        =      0.0326 MPa
   Wall shear stress - root-mean-square deviation     =      0.0255 MPa

   Frozen layer fraction - maximum                    =      1.0000
   Frozen layer fraction - 95th percentile            =      0.2312
   Frozen layer fraction - 5th percentile             =      0.0673
   Frozen layer fraction - minimum                    =      0.0000
   Frozen layer fraction - average                    =      0.1683
   Frozen layer fraction - root-mean-square deviation =      0.0752

   Shear rate - maximum                               =  1.3478E+04 1/s
   Shear rate - 95th percentile                       =    479.5600 1/s
   Shear rate - average                               =    105.8480 1/s
   Shear rate - root-mean-square deviation            =    275.1480 1/s

Packing phase results summary :

   Peak pressure - minimum             (at   0.000 s) =      0.0000 MPa
   Clamp force - maximum               (at   4.560 s) =    437.2186 tonne
   Total weight - maximum              (at  12.060 s) =   1173.6900 g

End of packing phase results summary :

   Time at the end of packing                         =     32.6548 s
   Total weight (part + runners)                      =   1170.8200 g

Packing phase results summary for the part :

   Bulk temperature - maximum          (at   2.650 s) =    237.8010 C
   Bulk temperature - 95th percentile  (at   2.650 s) =    233.5710 C
   Bulk temperature - 5th percentile   (at  32.655 s) =     53.7600 C
   Bulk temperature - minimum          (at  26.905 s) =     50.0000 C

   Wall shear stress - maximum         (at   9.060 s) =      4.0098 MPa
   Wall shear stress - 95th percentile (at  12.508 s) =      0.1104 MPa

   Volumetric shrinkage - maximum      (at   2.650 s) =     16.3553 %
   Volumetric shrinkage - 95th %ile    (at   2.650 s) =     13.5879 %
   Volumetric shrinkage - 5th %ile     (at  32.655 s) =      2.0501 %
   Volumetric shrinkage - minimum      (at   6.060 s) =     -0.2425 %

   Total part weight - maximum         (at  12.060 s) =   1173.6900 g

End of packing phase results summary for the part :

   Total part weight (excluding runners)              =   1170.8200 g

   Bulk temperature - maximum                         =     94.5460 C
   Bulk temperature - 95th percentile                 =     65.2840 C
   Bulk temperature - 5th percentile                  =     53.7600 C
   Bulk temperature - minimum                         =     50.0000 C
   Bulk temperature - average                         =     60.3300 C
   Bulk temperature - root-mean-square deviation      =      3.2764 C

   Frozen layer fraction - maximum                    =      1.0000
   Frozen layer fraction - 95th percentile            =      1.0000
   Frozen layer fraction - 5th percentile             =      1.0000
   Frozen layer fraction - minimum                    =      1.0000
   Frozen layer fraction - average                    =      1.0000
   Frozen layer fraction - root-mean-square deviation =      0.0000

   Volumetric shrinkage - maximum                     =     11.8736 %
   Volumetric shrinkage - 95th percentile             =      7.4253 %
   Volumetric shrinkage - 5th percentile              =      2.0501 %
   Volumetric shrinkage - minimum                     =      0.5023 %
   Volumetric shrinkage - average                     =      4.0689 %
   Volumetric shrinkage - root-mean-square deviation  =      1.5782 %

   Sink index - maximum                               =      0.4774 %
   Sink index - 95th percentile                       = -1.2167E-05 %
   Sink index - minimum                               =     -0.0282 %
   Sink index - root-mean-square deviation            =      0.1175 %

Preparing interface data...
  Preparing PPC file for cooling analysis...
  Preparing LSP file for warpage analysis...
Finished preparing the interface data

作者: wy9515301    时间: 2006-10-11 15:58
个人认为只要不是镜面的产品一般都没有问题。通常针点进胶和潜伏进胶都会在剪切速率及剪切应力上超标。如果你想不超标那加大浇口降低流速就行了。

       版主睡大觉去了哦，我这菜菜鸟出来抛块砖。这个版块冷成这样，关了算了。
作者: shirley_1999    时间: 2006-10-11 16:15
降低流速看看，调整工艺。
不过moldflow计算的shear rate 不是很准。
作者: zengshengqu    时间: 2006-10-11 20:39
我感觉点浇口剪切速率经常都会超，但时间短，位置小，一般是没问题
作者: luminghua88    时间: 2006-10-12 12:21
是的啊，在窗口中显示又是正常的！
作者: luminghua88    时间: 2006-10-12 12:32
此产品造成翘曲变形最大因素是体积收缩不均匀，冷却，和分子取向影响较小！请问还有一项“conner effect"怎么理解？是什么意思呢，在这个案例里它对变形也影响不大！
作者: luminghua88    时间: 2006-10-12 12:37
我想请问，造型收缩不均匀的因素是什么呢？是不是充填不均匀造成的啊！当然PP＋CaCo3的收缩是比较大的，设定为1.1％的收缩率！对此问题有没有好的解决措施！
作者: luminghua88    时间: 2006-10-12 12:42
来个填充时间图（FILL TIME）我觉得略有些流动不太平衡！请大家看一下！来参考参考！
作者: luminghua88    时间: 2006-10-12 12:51
对了，来张用MF分析的最佳浇口位置图！大家有什么好的建议浇口做在哪里较好（热流道）是不是MF分析的也不准啊！
作者: luminghua88    时间: 2006-10-13 15:14
我顶一下！
作者: navypeng    时间: 2006-10-20 16:25
我经常遇到这样的问题,SHAER RATIO经常超高,有的时候改浇口也不能达到要求
作者: 278385803    时间: 2006-10-26 15:27
1局部加热
2当料流到这个部位时，想办法把流数降下来。
3材料或设计不合理
我认为！
作者: 278385803    时间: 2006-10-26 15:28
1局部加热（加加热棒）
2当料流到这个部位时，想办法把流数降下来。
3材料或设计不合理
我认为！
作者: 小小XX    时间: 2007-2-9 18:16
定浇口是一个很重要的环节，要结合实际与MF分析结果来确定浇口，不能一味的只看MF分析结果。
作者: grace_cccn    时间: 2007-8-2 10:52
多多学习的好地方