| 性能项目 [td]试验条件[状态] [td]测试方法 [td]测试数据 [td]数据单位 |
| 物理性能 [td]比重 [td] [td]ASTM D-792 [td]1.05 [td] |
| 熔体流动速率 [td]220℃/10kg [td]ASTM D-1238 [td]6 [td]g/10min |
| 成型收缩率 [td] [td]ASTM D-955 [td]0.004-0.007 [td]mm/mm |
| 机械性能 [td]冲击弹度 [td]Notched1/4" [td]ASTM D-256 [td]16 [td]kgcm/cm |
| 延伸率 [td] [td]ASTM D-638 [td]25 [td]% |
| 洛氏硬度 [td]R-Scale [td]ASTM D-785 [td]104 [td] |
| 弯曲弹性率 [td] [td]ASTM D-790 [td]750 [td]kg/cm2 |
| 挠曲模量 [td] [td]ASTM D-790 [td]22000 [td]kg/cm2 |
| 拉伸强度 [td] [td]ASTM D-638 [td]460 [td]kg/cm2 |
| 电气性能 [td]HVTR [td] [td]UL-746A [td]2 [td]PLCCode |
| 抗弧光 [td] [td]ASTM D-495 [td]6 [td]PLCCode |
| HWI [td] [td]UL-746A [td]3 [td]PLCCode |
| CTI [td] [td]UL-746A [td]0 [td]PLCCode |
| HAI [td] [td]UL-746A [td]0 [td]PLCCode |
| 热性能 [td]热变形温度 [td]Unannealed18.5kg/cm²,1/2" [td]ASTM D-648 [td]103 [td]℃ |
| 燃烧率 [td]1/8" [td]UL-94 [td]HB [td] |
| 燃烧率 [td]1/16" [td]UL-94 [td]HB [td] |
| 维卡软化点 [td]1.000g [td]ASTM D-1525 [td]125 [td]℃ |
| 燃烧率 [td]1/8" [td]IEC-707 [td]FH3-33 [td]mm/min |