标题: 我做的一个气辅成型分析 [打印本页]

作者: TRYNEW 时间: 2005-5-5 09:41
标题: 我做的一个气辅成型分析
      气体可以走得很远，但是窜气比较严重，而且离气针较远处的气体吹空的体积很小。
      如何改善，请大家发表见解。谢谢！

作者: TRYNEW 时间: 2005-5-5 09:44
胶料的厚度（气道处的厚度是5mm，其他3mm）

作者: TRYNEW 时间: 2005-5-5 09:47
成型参数的设置：

Machine Name:    J1300EIII 5000H B
Material Name: Novodur PMTM : Bayer USA
------------------------------------------------------------------------Machine Specification:
------------------------------------------------------------------------
Maximum pressure:                            142.0000 MPa
Screw diameter:                               120.0000 mm
Maximum injection speed:                      89.3036 mm/s
Screw intensification ratio:                   10.0000
Machine response time:                         0.010 s
  Machine maximum clamp force:                1300.0000 tonne
------------------------------------------------------------------------Temperature Settings
------------------------------------------------------------------------Melt temperature:                            240.0000 C
Mold cavity_side temperature:                65.0000 C
Mold core-side temperature:                   65.0000 C
------------------------------------------------------------------------Injection Settings
------------------------------------------------------------------------Injection control method: Stroke vs ram speed
Injection profile:
         Ram position(mm)          Ram speed(mm/s)
          300.0000                23.2189
          290.0000                23.2189
          250.0000                89.3036
          150.0000                35.7214
           80.0000                4.4652
            5.0000                4.4652
            0.0000                4.4652
Packing pressure profile
          Duration                Pressure
             (s)                   (MPa)
            0.0000                51.3028
           11.1000                51.3028
Cooling time:                                  30.0000 s
------------------------------------------------------------------------Valve Gate Control Settings
------------------------------------------------------------------------ Valve gate opens and closes by:
         Control ID       Open                Close
         ----------    ------------          ------------
          1                0.0000 s             3.5000 s
------------------------------------------------------------------------Gas Injection Control Settings
------------------------------------------------------------------------Gas injection controller no. 1 :
   Material                                        = Compressed Nitrogen
   ID                                              = 1
   Gas injection control method                      = Pressure control
   Gas delay time                                  =    1.8000 s
   Gas injection time                               =    8.0000 s
   Gas pressure vs time profile:
           time (s)          pressure (MPa)
          ----------          -------------
            0.0000                0.0000
   Maximum gas pressure                            =    10.0000 MPa
   Number of gas entrances using this controller    =    4
   Timer for closing polymer injection location shut-off valve = 5.25 s
------------------------------------------------------------------------Results from Flow  Analysis
Total volume of the part and cold runners: 1566.8200 cm^3
Switch-over Pressure:                         64.1285 MPa
Maximum clamp force required:                768.4105 tonne

作者: chengx3655 时间: 2005-5-6 12:48
传来学习学习

作者: TRYNEW 时间: 2005-5-6 17:10

chengx3655 wrote:
传来学习学习

传什么啊？sdy图档？

作者: fly_snoopy 时间: 2005-5-6 17:12
某条件下的流动进气情况，由于流动不平衡，气体的进入方向有选择性

作者: TRYNEW 时间: 2005-5-7 10:41
      气体总是朝压力最小的方向前进。按道理，气针两边的气体是差不多的，而且在拐角处的窜气应该向外吧。moldex的结果似乎有点不合理。
      一己之见，欢迎讨论。

作者: fly_snoopy 时间: 2005-5-7 11:55
拐角处的窜气不明显，是因为我把拐角的气道做了调整，且进气位置也做了调整

作者: fly_snoopy 时间: 2005-5-7 12:03
气道是直角形状的，穿气明显一点

作者: fly_snoopy 时间: 2005-5-7 12:51
4点进胶流动平衡时候的进气情况如图

作者: fly_snoopy 时间: 2005-5-7 14:09
皮層比指氣輔射出成型在充填/保壓結束瞬間該點皮層塑
料所佔分率.
1代表該點全為塑料填滿 ;
小於1代表該點有部分塑料為氣體所掏空.

作者: TRYNEW 时间: 2005-5-9 15:42

fly_snoopy wrote:
皮層比指氣輔射出成型在充填/保壓結束瞬間該點皮層塑
  料所佔分率.
  1代表該點全為塑料填滿 ;
  小於1代表該點有部分塑料為氣體所掏空.

这个我知道。现在的问题是，远离气针处虽然有气体渗透，但皮层

太厚。有没有办法吹薄一点？

作者: fly_snoopy 时间: 2005-5-9 15:53
皮层薄厚不是目的，目的是不要让产品有变形尺寸稳定，气辅成型影响尺寸的因素很多，变一个条件尺寸就差很多，可能的情况下局部减少气体末端附近的肉厚，延长进气时间会有所帮助

作者: alijianhui 时间: 2006-8-6 22:25
你可以试试将塑料注射量和气体延迟时间都降小一些，这有助于皮层变薄。

作者: z30th 时间: 2006-8-19 19:04
试试把延迟时间减小点,气体压力也减小点.

作者: xhb1000 时间: 2008-2-26 14:21
Screw intensification ratio: 10.0000
翻译成中文的意思是？