liangyue

本人进行Cool + Flow.分析
Injection + packing + cooling time Automatic
Injection time        Automatic
Velocity/pressure switch-over        by % volume          =     99.0000 %
Pack/Holding Control        %Filling pressure vs time
Pack/Hold Profile          0   80%
10   80%
结果如下:
Cavity surface temperature - maximum                 = 194.2070 C
Cavity surface temperature - minimum                 =  33.7150 C
Cavity surface temperature - average                 =  43.1120 C
Average mold exterior temperature                    =  26.1130 C
Cycle time calculated from percentage frozen on average part thickness
Cycle time                                           =  10.5505 s


Process parameters :   
   ------------------
   Fill time                                          =      1.7850 s
   Injection time has been determined by automatic calculation.
   Stroke volume determination                        = Automatic
   Cycle time                                         =     10.5505 s

   Velocity/pressure switch-over by % volume          =     99.0000 %
   Packing/holding time                               =     10.0000 s
   Pack/hold pressure profile (rel):
          duration  % filling pressure
     ---------------------------------
            0.0000 s           80.0000
           10.0000 s           80.0000
   Ambient temperature                                =     25.0000 C
   Melt temperature                                   =    235.0000 C
   Ideal cavity-side mold temperature                 =     60.0000 C
   Ideal core-side mold temperature                   =     60.0000 C

   NOTE: Using mold wall temperature data from cooling analysis


Packing phase:
|-------------------------------------------------------------|
|  Time  |Packing|  Pressure   | Clamp force|      Status     |
|  (s)   |  (%)  |    (MPa)    |  (tonne)   |                 |
|-------------------------------------------------------------|
|   2.16 |  0.00 |       73.07 |      13.84 |        P        |
|   2.50 | 10.07 |       73.07 |      17.51 |        P        |
|   3.00 | 24.81 |       73.07 |      16.29 |        P        |
|   3.50 | 39.55 |       73.07 |      13.91 |        P        |
|   4.00 | 54.29 |       73.07 |      11.28 |        P        |
|   4.50 | 69.03 |       73.07 |       9.43 |        P        |
|   5.00 | 83.77 |       73.07 |       8.15 |        P        |
|   5.50 | 98.51 |       73.07 |       7.09 |        P        |
|   6.00 |100.00 |       73.07 |       6.34 |        P        |
|   6.50 |100.00 |       73.07 |       5.79 |        P        |
|   7.00 |100.00 |       73.07 |       5.36 |        P        |
|   7.50 |100.00 |       73.07 |       5.03 |        P        |
|   8.00 |100.00 |       73.07 |       4.75 |        P        |
|   8.25 |100.00 |       73.07 |       4.64 |        P        |
|   8.50 |100.00 |       73.07 |       4.53 |        P        |
|   8.75 |100.00 |       73.07 |       4.42 |        P        |
|   9.00 |100.00 |       73.07 |       4.33 |        P        |
|   9.25 |100.00 |       73.07 |       4.24 |        P        |
|   9.50 |100.00 |       73.07 |       4.15 |        P        |
|   9.75 |100.00 |       73.07 |       4.07 |        P        |
|  10.00 |100.00 |       73.07 |       3.99 |        P        |
|   1.91 | 96.21 |       91.33 |      14.03 |    7.99 |  V/P  |
|  11.00 |100.00 |       73.07 |       3.72 |        P      

是不是成型周期为Cycle time   =     10.5505 s,那冷却时间又该是多少
保压是否到6S就够|   6.50 |100.00 |       73.07 |       5.79 |        P        |
|   1.91 | 96.21 |       91.33 |      14.03 |    7.99 |  V/P  |是什么意识

[ 本帖最后由 liangyue 于 2007-4-5 16:31 编辑 ]